Supression of Water Treeing by BN nanosheet in XLPE nanocomposites subjected to tensile stress
编号:55
访问权限:仅限参会人
更新:2022-08-29 10:59:58 浏览:79次
口头报告
摘要
Purpose/Aim
By using organic nanoparticles to modify the polymer, the water tree resistance of insulating materials can be effectively improved and the occurrence of water branches can be reduced. However, there are few studies on inhibiting water tree growth through two-dimension nanoparticles. This work focuses on the water treeing supression by 2D BNNs, espercailly treated by tensile stress.
Experimental/Modeling methods
XLPE/BNNs nanocomposites were selected as experimental materials. XLPE/BNNs composites with different mass fractions (1wt%,3wt%,5wt% and 10wt%) were prepared.The specimens are in the shape of a disc with a diameter of (35±1) mm and a thickness of (5.0±0.1) mm. Seven defects are manufactured in the sample. The radius of the defect tip is (40±1) µm, the included angle is 28°, the diameter of the defect tip is 1.0 mm, and the defect depth is 3mm.The water tree development was carried out by plaque test AC accelerated aging method. Before experiments, the samples are stretched. The treeing growth results were discussed by polarizing microscope and SEM.
Results/discussion
The 2D nanostructures of BNNs can hinder the growth of water branches and reduce the growth length of water tree; It can be found that the higher the concentration of BN, the smaller the length of the horizontal direction of the water tree. After tensile stress, the treeing growth becomes wider in the parallel direction.
Conclusions
The flake structure of BN can effectively inhibit the growth of branches. Thensile stress could extend the water treeing branches by introducing more Capillary channel of water.
关键词
XLPE/BNNs composites;tensile stress;water tree